TECAPEEK natural

Material Name: Tecapeek natural

Color: beige

Molding Method: extrusion 

Stock Shapes: rod / sheet / tube

Cut to Size: available

Free Sample: available

Payment: T/T, VISA, MasterCard, Western Union, PayPal

TECAPEEK Unfilled

TECAPEEK® (Polyetheretherketone) natural is a virgin PEEK from Ensinger. This type of PEEK uses Victrex polymer as raw material. Tecapeek shows a very high working temperature of up to 260℃ and very high mechanical strength. Also, Tecapeek demonstrates excellent chemical resistance that could be applied in the hash working environment. 

TECAPEEK Features

  • high heat deflection temperature
  • excellent chemical resistance
  • very good machinability 
  • high creep resistance 
  • resistance to steam 
  • very good dimensional stability 

TECAPEEK Facts

Chemical designation

PEEK (Polyetheretherketone)


Colour

beige


Density

1,31 g/cm3


Target Industries

  • automotive technology
  • mechanical engineering
  • aviation technology
  • chemical technology  
  • vacuum industry
  • food industry 

TECAPEEK Stock Shapes

Rods&Tubes

Material Diameter Length Color
PEEK Rod
Ø6....210mm
1000mm
beige
PEEK tube
Exterior: Ø 30… 380 mm Interior: Ø 20… 300 mm
1000mm
beige

Sheets

Material Thickness Dimension Color
PEEK sheet
6....150mm
500*1000mm
beige

TECAPEEK Properties

Value

Parameter

Unit

Norm

Tensile strength

107

50 mm/min

Mpa

DIN EN ISO 527-2

Modulus of elasticity (tensile test)

4000

1mm/min

Mpa

DIN EN ISO 527-2

Tensile strength at yield

107

50 mm/min

Mpa

DIN EN ISO 527-2

Elongation at break (tensile test)

35

50 mm/min

%

DIN EN ISO 527-2

Flexural strength

156

2 mm/min, 10N

Mpa

DIN EN ISO 178

Modulus of elasticity (flexural test)

4000

2 mm/min, 10N

Mpa

DIN EN ISO 178

Compression strength 

25/53/125

1%/2%/5% 5 mm/min, 10N

Mpa

EN ISO 604

Compression modulus

3000

5 mm/min, 10N

Mpa

EN ISO 604

Impact strength (Charpy)

n.b.

max 7.5J

KJ/m2

DIN EN ISO 179-1eU

Notched impact strength (Charpy)

5

max 7.5J

KJ/m2

DIN EN ISO 179-1eA

Ball indentation hardness

230

Mpa

ISO 2039-1

Value

Parameter

Unit

Norm

Glass transition temperature

150

/

DIN EN ISO 11357

Melting temperature

341

/

DIN EN ISO 11357

Service temperature 

260

long term 

/

Service temperature 

300

short term 

/

Thermal expansion (CLTE)

5

23-60℃, long

10-5K-1

DIN EN ISO 11359-1;2

Thermal expansion (CLTE)

5

23-100℃, long

10-5K-1

DIN EN ISO 11359-1;2

Thermal expansion (CLTE)

7

100-150℃, long

10-5K-1

DIN EN ISO 11359-1;2

Value

Parameter

Unit

Norm

Surface resistivity

10^15

sliver electrode, 23°C

Ω

DIN IEC 60093

Volume resistivity

10^15

sliver electrode, 23°C

Ω*cm

DIN IEC 60093

Value

Parameter

Unit

Norm

Flammability (UL94)

V-0

corresponding to 

/

DIN IEC 60695-11-10

Water absorption

0.02/0.03

24 h/96 h , 23°C

%

DIN EN ISO 62

Resistance to hot water/bases

good resistance (+)

/

/

/

Resistance to weathering

poor resistance (-)

/

/

/